GEECLAD 16/18 Kt.

Decorative coating.

High alloy cyanide silver – gold bath. Producing a fully bright pale yellow 16/18 Karat deposit for economical thickness build-up.

GEECLAD 5N

Decorative coating to produce rose gold colour.

 

High alloy Gold-Copper-Cadmium plating solution. Designed to produce a fully bright tarnish free rose gold color of 18-20 Kt purity used in jewellery, watches and novelties.

GEECLAD 1N/2N/3N

Decorative coating

Acid gold bath gives a tarnish free, wear resistant deposit matching the NIHS 2N18 and NIHS 3N18 colors.

Please reload

GEECLAD SERIES DECORATIVE

GEEFORM SERIES

GEESTRIKE SERIES

GEEFLASH SERIES

GEEFORM 18 KDF

For electroforming of 14 and 18 Karat fine jewelry.

Cadmium free cyanide based process for electroforming 14-18 Karat jewelry. High brightness, no nodules, stress free, excellent throwing power. Cyanide free replenishers.

GEEFORM 2022 KDF

For electroforming of 21 & 22 Karat fine jewelry.

Low gold content copper, gold alloy cyanide based process for electroforming 21-22 Karat jewelry. Very stable relationship between current density and efficiency, high brightness no nodules, excellent throwing power, stress free after annealing.

GEEFORM MATTE 24C

For electroforming of 24 Karat hollow statues with Matte finish.

Neutral, high speed pure gold forming bath. Designed for electroforming idols, jewelry and novelty items. The matte yellow finely structured deposit has excellent ductility and fully stress free.

Please reload

GEEFORM SEMI-BRIGHT 24C

For electroforming of 24 Karat hollow statues with semi bright finish.

Neutral, high speed pure gold forming bath. Designed for electroforming idols and jewelry items. The yellow finely structured deposit has excellent soldering properties.

GEEFORM 2024 S

For electroforming of 24 Karat hollow statues. Also finds its applications in making dental caps.

An ammonia free Sulphite based forming process for forming jewelry items and statues. Deposits are mirror bright, very hard yet ductile. Also used in dentistry for making dental caps

Please reload

GEESTRIKE TE

Gold strike prior to final coating.

Acid gold bath designed to provide a thin adherent film of gold on activated substrates such as brass, iron prior to application of thicker deposits.

GEESTRIKE TB

Gold strike prior to final coating. Also finds application as a final finish.

Acid gold bath designed to provide a thin rich colored adherent film of gold on substrates such as brass or nickel plated brass bangles in jewelry. Also used as a final color for costume jewelry.

Please reload

GEESTRIKE TS

Gold strike directly on stainless steel. Also as a final finish on stainless steel cutlery, surgical instruments, etc.

This strongly acidic gold strike bath is specifically designed to allow deposition of an adherent gold deposit directly onto normally passive surfaces like stainless steel, chromium, bright nickel, kovar, etc.

GEESTRIKE ECO-TS

Gold strike directly on stainless steel to get 1N/2N colors.

 

Strongly acidic gold strike bath to produce 1N/2N color deposits directly on stainless steel, kovar, etc. Bright up to 1.5-micron thickness. Casting is bio compatible.

Please reload

GEEFLASH 1N, 2N, 3N, 4N, 5N and champagne

Final coloring process

 

Alkaline low cyanide gold flash coating designed for final coloring of jewelry.

Please reload

GEECLAD N14

Decorative coating

 

Gives a tarnish free, wear resistant, pale yellow deposit matching the American 14 Karat color. Fully bright for any reasonable thickness.

GEECLAD P 308

Decorative coating.

Sulphite gold process giving a pale pink, mirror bright 22 Karat copper alloy. Deposit is pore free, hard and fine grained. This process is completely cyanide free and is used extensively in spectacle frame industry.

GEECLAD 1N/2N/3N

Decorative coating

Acid gold bath gives a tarnish free, wear resistant deposit matching the NIHS 2N18 and NIHS 3N18 colors.